DIN Ck10/1.1121 Engineering steel
Port: Hu nan
Ck10 engineering steel, Ck10 alloy tool steel, Ck10 alloy steel, Ck10 alloy structural steel
Alloy Structural Steel, Alloy Tool Steel, Carbon Structural Steel, Carbon Tool Steel, Bearing Steel, Spring Steel ,Stainless Steel, Refractory Steel, Roll Steel, Pinion Steel. Additionally, the company also has the capacity to forge round steel, steel flat, square steel, module, shaft and roller
1: Ck10 steel introduction
Ck10 has good plasticity and toughness, easy to be formed by cold and hot machining, good machinability after normalizing or cold machining, excellent weldability, no temper brittleness, poor hardenability and hardenability.
2: Ck10 steel equivalent
| Country | China | Japan | Germany | USA |
| Standard | GB/T | JIS |
DIN (W-Nr.) DIN 17210 |
AISI/ASTM |
| Grade |
|
|
Ck10 |
|
3: Ck10 steel chemical composition
| Grade | C | Si | Mn | P | S |
| Ck10 | 0.07-0.13 | 0.40 | 0.30-0.60 | 0.035 |
0.035 |
4: Ck10 steel mechanical properties
The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.
5: Ck10 steel overviews
| Size | Round | Dia 6-1200mm |
| Plate/Flat/Block |
Thickness 6mm-500mm |
|
|
Width 20mm-1000mm |
||
| Heat treatment | Normalized ; Annealed ; Quenched ; Tempered | |
| Surface condition | Black; Peeled; Polished; Machined; Grinded; Turned; Milled | |
| Delivery condition | Forged; Hot rolled; Cold drawn | |
| Test | Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. | |
| Payment terms | T/T;L/C;/Money gram/ Paypal | |
| Trade terms | FOB; CIF; C&F; etc.. | |
| Delivery time | 30-45 days | |
| Application | Ck10 is applied to automobile body, receptacle, deep drawing vessel, pipe, gasket, etc. It can also be used as a carburized member and a carbonitriding member with low core strength. | |
6: Delivery condition
For hot forged bar, usually the delivery condition is hot forged, annealed/QT, rough turned/Black surface.
For hot rolled bar, usually the delivery condition is hot rolled, annealed/QT, Black surface.
For hot forged block, usually the delivery condition is hot forged, annealed/QT, milled surface/Black surface
For hot rolled plate, usually the delivery condition is hot rolled, annealed/QT, black surface.
For cold drawn bar, usually the delivery condition is cold drawn, annealed/QT, peeled/black surface