Your present location:Home > Products > Tool steel

hot forged 1.2083 Plastic mould steels

Port: Hu nan

Supply Ability: 50000 Ton/Tons per Month

Min.Order Quantity: 0.1 Ton/Tons

E-mail:export@qilucs.com

  • Quick Details

    Steel Grade: 1.2083 /X40Cr14 / SUS420J2/ 4Cr13
    Standard: AISI, ASTM, BS, DIN, GB, JIS
    Dimensions: Dia 2mm~1500mm
    Place of Origin: Liaoning, China (Mainland)
    Brand Name: Neworigin
    Model Number: 1.2083 /X40Cr14 / SUS420J2/ 4Cr13
    Technique: Hot Rolled
    Application: Plastic mould steel
    Alloy Or Not: Is Alloy
    Special Use: Mold Steel
    Type: Alloy Steel Bar
    Product Name: hot forged 1.2083 Plastic mould steels
    Surface Treatment:black/polished/machined/peeled/grinded/turned
    Warranty: MTC / 3.1B
    Shape: flat /sheet/round bar
    Hardness: 52-56 HRC (Quenched)
    Certification: ISO9001, SGS, REACH, API
    Delivery condition: Hot rolled or forged, Peeled or black surface, annealed or QT.
    Inspection: UT, Mechanics, Physical testing, Chemical component analysis
    Our product line: Tool steel, Carbon structural steel, Alloy structural steel
    Annual turn over: USD 140,000,000.00
    Packaging & Delivery

    Packaging Details: 20ft: GW:17.5T; (5.69mX2.13mX2.18m,) 
    40ft: GW:22T; (11.8mX2.13mX2.18m,)

    Delivery Detail: 4~7 days


    hot forged 1.2083 Plastic mould steels

    General Information:

    Stainless martensitic steel with a high hardenability, good polishing properties, excellent resistance to corrosion and hot oxidation.

     

    Application:

    Used for plastic moulds, particularly for acid aggressive plastics (e.g. acetate and PVC), or plastics containing abrasive fillers. Suited for the manufacture of glass, such as moulds of optical products.


    Comparable Standards:                                                                                                       

    AISI/SAE DIN W.Nr. AFNOR JIS BS SIAU GB,YB

    -

    X40Cr14 1.2083 - SUS420J2 - - 4Cr13

     

     Chemical Analysis (%):                                                                                                         

    C Mn Si Cr Ni Mo P S
    0.36-0.42 ≤1.00 ≤1.00 12.5-14.5 - - ≤0.03 ≤0.03

       

    Heat treatment                                                                                                        

    Annealing:

    -Heat to 750~800°C, with hold at minimum rate for 3 hours.

    -Furnace cooling.

     

    Stress relieving:

    To be carried out after machining and before the final heat treatment.

    Heating to 600~650°C for 2 hours.

     

    Hardening:

    Preheating to 600~700°C;

    - Austenitizing at 990~1040°C

    - Oil or thermal bath cooling at 500~550°C, then oil cooling according to the steel shape and size.

    Quenched hardness: HRC 52~56

     

    Tempering:

    To be carried out after hardening according to the required hardness; at 170-270 °C in order to match hardness and resistance to corrosion; permanence for at least 2 hours;

    Tempering must be repeated at least twice at a temperature 30 °C lower than the previous. Cooling in air.