DIN 16NiCr4/1.5714 | BS EN351/635M15 Engineering Steel

Port: Hu nan

engineering steel, cold work tool steel, hot work tool steel, plastic mold steel, spring steel, high speed steel, stainless steel

Alloy Structural Steel, Alloy Tool Steel, Carbon Structural Steel, Carbon Tool Steel, Bearing Steel, Spring Steel ,Stainless Steel, Refractory Steel, Roll Steel, Pinion Steel. Additionally, the company also has the capacity to forge round steel, steel flat, square steel, module, shaft and roller


  • DIN 16NiCr4 1.5714 BS EN351 635M15 Steel Plate

    1: 16NiCr4 steel introduction

        16NiCr4 Alloy steel is a low carbon case hardening steel which has at least 0.6Cr%,0.8%Ni as strengthening elements. It has a low-medium hardenability with good core resistance up to a thickness of about 50 mm, and had good machinability in the annealed condition.16NiCr4 is generally supplied in the annealed condition with Max hardness 217HB.

    2: 16NiCr4 Steel equivalent
    Country Germany USA
    Standard EN10250 BS 970
    Grade 16NiCr4/1.5714
    3: 16NiCr4 steel chemical composition
    Grade C Mn Si P S Cr Ni
    0.13-0.19 0.70-1.00 0.40 max 0.025 max 0.035 max 0.60-1.00 0.80-1.10

    4: 16NiCr4 steel mechanical properties  

        The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as normalized, tempered, QT. If you want to know the properties, kindly contact the salesman.

    5: 16NiCr4 steel overviews
    Size Round Dia 6-1000mm
    Plate/Flat/Block Thickness
    Heat treatment Normalized ; Annealed ; Quenched ; Tempered
    Surface condition Black; Peeled; Polished; Machined; Grinded; Turned; Milled
    Delivery condition Forged; Hot rolled; Cold drawn
    Test Tensile strength, Yield strength, elongation, area of reduction, impact value, hardness, grain size, ultrasonic test, US inspection, magnetic particle testing, etc. 
    Payment terms T/T;L/C;/Money gram/ Paypal
    Trade terms FOB; CIF; C&F; etc..
    Delivery time 30-45 days
    Application 16NiCr4 Alloy steel is a case-hardening steel widely used for high-strength core parts, structural parts subject to abrasion and variable loads typically used for small-sized parts, such as loaded gears, screws, pins, shafts, pivots, machine parts, cars and engines

    6. Heat Treatment

        16NiCr4 Alloy steel forging temperature:900 – 1150°C, cooled as slowly as possible in still air or in the sand after forged.
    Heat Treatment
        Normalizing: 870 – 890°C, Cooling in air
        Soft Annealing:680 – 720°C, Cooling in the furnace
        Core-hardening:850-890°C,oil-polymer salt bath
        Case-hardening:780-820°C,oil-polymer salt bath
    Surface Hardness
        Treated to improve wearability(+S): Max 255HB
        Soft annealed(+A): Max 217HB
        Treated to hardness range(+TH):166-217HB
        Treated to ferrite-pearlite structure and hardness range(+FP):156-207HB

    7: Delivery condition
        For hot forged rolled bar, usually the delivery condition is hot forged or rolled, annealed/QT, rough turned/Black surface.
        For hot forged or hot rolled bar, usually the delivery condition is hot rolled, annealed/QT, Black surface.
        For hot forged plate, usually the delivery condition is hot forged, annealed/QT, milled surface/Black surface.
        For hot rolled plate, usually the delivery condition is hot rolled, annealed/QT, black surface.